Polyetherimide
Recycled materials
Data
| Properties | Standards | Test Conditions | Units | Recycled | |||
| RPEI-10 | RPEI-10G30 (GF 30%) |
Mechanical Properties
| Izod Impact Strength | ASTM D256 | V-Notched 1/8" 23℃ | J/m | 30 | 125 | ||
| ASTM D4812 | Unnotched 1/8" 23℃ | No break | 837 | ||||
| Tensile Strength at break | ISO 527 | 4.0t 23℃ | MPa | 110 | 110 | ||
| Tensile Elongation at break | ISO 527 | 4.0t 23℃ | % | 13 | 5 | ||
| Flexural Strength | ISO 178 | 4.0t 23℃ | MPa | 165 | 275 | ||
| Flexural Modulus | ISO 178 | 4.0t 23℃ | MPa | 3500 | 11900 | ||
| Rockwell Hardness | R scale | --- | --- | --- | --- |
Thermal Properties
| Dielectric Breakdown Strength | ASTM D149 | --- | kV/mm | 33 | 25 | ||
| Dielectric Constant | ASTM D150 | 10^6 Hz | --- | 3.15 | 3.7 | ||
| Dielectric Dissipation Factor | ASTM D150 | 10^6 Hz | --- | 0.001 | 10^6 Hz | 0.0015 | 10^6 Hz |
| Volume Resistivity | ASTM D257 | --- | Ω・cm | 10^16 | 10^16 |
Physical Properties
| Specific Gravity | ASTM D792 | --- | --- | 1.28 | 1.51 | ||
| Water Absorption | ASTM D570 | 24 hrs @23℃ Water immersion | % | --- | 0.16 | ||
| Mould Shrinkage | ISO 294 | Parallel | % | 0.5 ~ 0.7 | 0.2 ~ 0.4 | ||
| Across | 0.2 ~ 0.5 |
Electrical Properties
| Flammability | UL94 | --- | -- | (Equiv. V-0) (1.7 mm) | (Equiv. V-0) (1.7 mm) | ||
| Heat Deflection Temperature | ISO 75 | 1.82MPa | ℃ | 197 | --- | ||
| ℉ | 386 | --- | |||||
| JIS K7191-2 | 1.82MPa | ℃ | --- | 220 | |||
| ℉ | --- | 428 | |||||
| Melt Flow Rate | ISO 1133-1 | 337℃ 5.0 kgf | g/10 min. | 12 | --- |
* The values contained herein are typical, based on general molding conditions.